Response of Plasma-Polymerized Hexamethyldisiloxane Films to Aqueous Environments.

Thin plasma polymer films were deposited in hexamethyldisiloxane (HMDSO) and HMDSO/O2 low-pressure discharges and their chemical structures analyzed using infrared (IR) spectroscopy and neutron reflectometry (NR). The (plasma-polymerized) ppHMDSO film exhibits hydrophobic, poly(dimethylsiloxane)-like properties, while the retention of carbon groups is reduced by O2 addition, yielding a more inorganic, hydrophilic ppSiOx film. Both films show a minor (vertical) density gradient perpendicular to the substrate, where the exposed film surface seems to be more oxidized, indicating oxidative aging reactions upon contact with air. The hydration and water uptake abilities of the films in aqueous environments were investigated in humid environments using ellipsometry, NR in D2O, and multiple transmission-reflection IR measurements after equilibration of the films in water.

Metal fluoride-based transparent nanocomposites with low refractive indices.

The utilisation of magnesium and aluminium fluoride nanoparticles in the preparation of transparent composites leading to materials with superior properties was investigated. Nanoscopic magnesium and aluminium fluoride has been prepared by the fluorolytic sol-gel route from the alkoxides and was surface modified by the reaction with trifluoroacetic acid or perfluorobutyric acid. IR spectroscopic experiments of the xerogels and crystal structure analysis of a trinuclear [Mg3(µ3F)(µ-TFA)6(OCH3)2(py)](3-) cluster unit indicate that the carboxylate group is bound to the particle surface in a monodentate or bidentate bridging fashion. These particles were successfully incorporated into acrylate polymers with up to 40 wt% content to give fully transparent material. Ellipsometry and m-line measurements of thin films show the reduction of the refractive index of composite films with increasing metal fluoride filler content.